Blog

Oil return and bubbling2

After the hot transfer film is printed, small bubbles of different sizes appear on the adhesive back surface, and there are cracking marks.

view more

Ink accumulation, ink mixing, and ink flow problems2

Inquire about local temperature and humidity, and observe the temperature and humidity control of customer workshop ask when it appeared

view more

Ink accumulation, ink mixing, and ink flow problems1

① Ink settling The ink has settled in the bottle
② Membrane moisture
③ Adjusting the curve, Membrane and used Poor white ink

view more

Sharp pattern fracture problem

Sharp patterns, such as lines, sharp corners and other patterns, when peeling off, the pattern breaks or warps at the corners

view more

Sawtooth edge problem on one side

After pressing and tearing off, there is a slight serrated edge on one side, but no such phenomenon on the other side

view more

Not easy to peel off

Difficult to tear after pressing
Severe jamming when tearing off
When tearing off, the pattern cannot be completely transferred to the f

view more

Print white dots

After shaking the powder and baking, white spots appear when viewed from the front of the pattern; Looking at the back, there are colored ink dots rev

view more

Snowflake points

① Ink is incompatible with heat transfer film
② The amount of black ink is too large, and the drying in front of the powder shaker is insuffici

view more

Tear off and delaminate after pressing

When pressing and tearing off, the hot melt adhesive layer and the white ink layer are separated

view more

Oil return and bubbling

The hot transfer film fails to be hot stamped on the material in time after printing. After being put on hold for a period of time, oily liquid will a

view more

Pattern anti-sticking

After printing and rewinding, the printed layer is adhered to the back of the film, which affects the integrity of the pattern

view more

Mixed ink phenomenon

The topcoat is bumped and falls off, causing color ink and white ink to mix after printing
White patches on unprinted membrane surfaces

view more