Renewables

I'm green bio-based^TM Ethylene Vinyl Acetate Copolymer

SVT2180 / SVT2180N

Melt Flow Rate (190°C/2.16kg)

ASTM D 1238

2.1 g/10 min

Vinyl-Acetate Content

ASTM-D-5594-98

19 %

Density

D 1505 / D 792

0.940 g/cm³

Tensile Strength at Break

D 638

19 MPa

I'm green bio-based^TM Polyethylene - Low Density

SBF0323HC

Melt Flow Rate (190°C/2.16kg)

D 1238

0.32 g/10 min

Density

D 1505

0.923 g/cm³

Tensile Strength at Break (MD/TD)

D 882

20/20 MPa

Elongation at Break (MD/TD)

D 882

390/930 %

I'm green bio-based^TM Polyethylene - Low Density

SEB853

Melt Flow Rate (190°C/2.16kg)

D 1238

2.7 g/10 min

Density

D 1505

0.923 g/cm³

Tensile Strength at Break (MD/TD)

D 882

25/20 MPa

Elongation at Break (MD/TD)

D 882

350/1050 %

I'm green bio-based^TM Polyethylene - Low Density

SEB853/72

Melt Flow Rate (190°C/2.16kg)

D 1238

2.7 g/10 min

Density

D 1505

0.923 g/cm³

Tensile Strength at Break (MD/TD)

D 882

25/20 MPa

Elongation at Break (MD/TD)

D 882

350/1050 %

I'm green bio-based^TM Polyethylene - Low Density

SLD4004

Melt Flow Rate (190°C/2.16kg)

ASTM D 1238

2.0 g/10 min

Density

ASTM D 792

0.923 g/cm³

Tensile Strength at Break (a)

ASTM D 638

13 MPa

Elongation at Break (a)

ASTM D 638

920 %

I'm green bio-based^TM Polyethylene - Low Density

SPB208

Melt Flow Rate (190°C/2.16kg)

D 1238

22 g/10 min

Density

D 1505

0.923 g/cm³

Tensile Strength at Yield (a)

D 638

10 MPa

Tensile Strength at Yield (a)

D 638

10 MPa

I'm green bio-based^TM Polyethylene - Low Density

SPB608

Melt Flow Rate (190°C/2.16kg)

D 1238

30 g/10 min

Density

D 1505

0.915 g/cm³

Tensile Strength at Yield (a)

D 638

8 MPa

Tensile Strength at Yield (a)

D 638

8 MPa

I'm green bio-based^TM Polyethylene - Low Density

SPB681

Melt Flow Rate (190°C/2.16kg)

D 1238

3.8 g/10 min

Density

D 1505

0.922 g/cm³

Tensile Strength at Break (MD/TD)

D 882

23/14 MPa

Elongation at Break (MD/TD)

D 882

370/875 %

I'm green bio-based^TM Polyethylene - Low Density

SPB681/59

Melt Flow Rate (190°C/2.16kg)

D 1238

3.8 g/10 min

Density

D 1505

0.922 g/cm³

Tensile Strength at Break (MD/TD)

D 882

23/14 MPa

Elongation at Break (MD/TD)

D 882

370/875 %

I'm green bio-based^TM Polyethylene - Low Density

STN7006

Melt Flow Rate (190°C/2.16kg)

D 1238

0.60 g/10 min

Density

D 1505

0.924 g/cm³

Tensile Strength at Break (MD/TD)

D 882

25/20 MPa

Elongation at Break (MD/TD)

D 882

280/870 %

I'm green bio-based^TM Polyethylene - Low Density

STS7006

Melt Flow Rate (190°C/2.16kg)

D 1238

0.60 g/10 min

Density

D 1505

0.925 g/cm³

Tensile Strength at Break (MD/TD)

D 882

25/20 MPa

Elongation at Break (MD/TD)

D 882

280/870 %

I'm green bio-based^TM Polyethylene - High Density

SGD4960

Melt Flow Rate (190°C/2.16kg)

D 1238

0.7 g/10 min

Melt Flow Rate (190°C/2.16kg)

ASTM D 1238

0.7 g/10 min

Melt Flow Rate (190°C/21.6kg)

D 1238

50 g/10 min

Density

ASTM D 792

0.962 g/cm³

I'm green bio-based^TM Polyethylene - High Density

SGM9450F

Melt Flow Rate (190°C/5kg)

ASTM D 1238

0.33 g/10 min

Melt Flow Rate (190°C/21.6kg)

D 1238

9.3 g/10 min

Density

D 792

0.952 g/cm³

Tensile Strength at Break (MD/TD)

D 882

85/45 MPa

I'm green bio-based^TM Polyethylene - High Density

SHA7260

Melt Flow Rate (190°C/2.16kg)

D 1238

20 g/10 min

Density

D 792

0.955 g/cm³

Density

ISO 1183-1

0.955 g/cm³

Melt Flow Rate (190°C/2,16 kg)

ISO 1133

20 g/10 min

I'm green bio-based^TM Polyethylene - High Density

SHC7260

Melt Flow Rate (190°C/2.16kg)

D 1238

7.2 g/10 min

Density

D 792

0.959 g/cm³

Density

ISO 1183-1

0.959 g/cm³

Melt Flow Rate (190°C/2,16 kg)

ISO 1133

7.2 g/10 min

I'm green bio-based^TM Polyethylene - Linear Low Density

SLH0820/30AF

Melt Flow Rate (190°C/2.16kg)

D 1238

0.8 g/10 min

Density

D 1505

0.920 g/cm³

Tensile Strength at Break (MD/TD)

D 882

40/40 MPa

Elongation at Break (MD/TD)

D 882

1190/1370 %

I'm green bio-based^TM Polyethylene - Linear Low Density

SLH118

Melt Flow Rate (190°C/2.16kg)

D 1238

1.0 g/10 min

Density

D 1505

0.916 g/cm³

Tensile Strength at Break (MD/TD)

D 882

40/40 MPa

Elongation at Break (MD/TD)

D 882

1080/1360 %

I'm green bio-based^TM Polyethylene - Linear Low Density

SLH218

Melt Flow Rate (190°C/2.16kg)

D 1238

2.3 g/10 min

Density

D 1505

0.916 g/cm³

Highlight - Ultimate Test (1)(2)

D 4649

400 %

Highlight - Puncture (1)(2)

D 4649

2.6 kg

I'm green bio-based^TM Polyethylene - Linear Low Density

SLL118

Melt Flow Rate (190°C/2.16kg)

D 1238

1.0 g/10 min

Density

D 1505

0.916 g/cm³

Tensile Strength at Break (MD/TD)

D 882

50/40 MPa

Elongation at Break (MD/TD)

D 882

1130/1430 %

I'm green bio-based^TM Polyethylene - Linear Low Density

SLL118/21

Melt Flow Rate (190°C/2.16kg)

D 1238

1.0 g/10 min

Density

D 792

0.918 g/cm³

Tensile Strength at Break (MD/TD)

D 882

40/30 MPa

Elongation at Break (MD/TD)

D 882

1070/1340 %

I'm green bio-based^TM Polyethylene - Linear Low Density

SLL318

Melt Flow Rate (190°C/2.16kg)

D 1238

2.7 g/10 min

Density

D 1505

0.918 g/cm³

Tensile Strength at Break (MD/TD)

D 882

30/30 MPa

Elongation at Break (MD/TD)

D 882

1220/1440 %

I'm green bio-based^TM Polyethylene - Low Density

SBC818

Melt Flow Rate (190°C/2.16kg)

D 1238

8.3 g/10 min

Density

D 1505

0.918 g/cm³

Tensile Strength at Break (MD/TD)

D 882

25/20 MPa

Elongation at Break (MD/TD)

D 882

380/870 %

I'm green bio-based^TM Polyethylene - Low Density

SBC818R50

Melt Flow Rate (190°C/2.16kg)

D 1238

8.3 g/10 min

Density

D 1505

0.918 g/cm³

Tensile Strength at Break (MD/TD)

D 882

25/20 MPa

Elongation at Break (MD/TD)

D 882

380/870 %

I'm green bio-based^TM Polyethylene - Low Density

SBF0323/12HC

Melt Flow Rate (190°C/2.16kg)

D 1238

0.32 g/10 min

Density

D 1505

0.923 g/cm³

Tensile Strength at Break (MD/TD)

D 882

20/20 MPa

Elongation at Break (MD/TD)

D 882

390/930 %